共沉淀法制备PDP用红色荧光粉 (Y, Gd)BO₃ : Eu³⁺的正交实验研究

材料物理和化学 | 更新时间：2020-08-12

- 共沉淀法制备PDP用红色荧光粉 (Y, Gd)BO₃ : Eu³⁺的正交实验研究
- Preparation of Red Phosphor (Y, Gd)BO₃ : Eu³⁺ by Coprecipitation Method with Orthogonal Test
- 液晶与显示 2009年24卷第5期页码：645-649
- 作者机构：
  
  1. 中国地质大学材料科学与化学工程学院,湖北武汉,430074
  2. 中国地质大学教育部纳米矿物材料及应用工程研究中心,湖北武汉 430074,E-mail:yanqi726@163.com
  3. 吉林大学测试中心,吉林长春,130026
- 作者简介：
- 基金信息：
- DOI：
  中图分类号： TN104.3
- 收稿日期：2009-03-20，
  
  修回日期：1900-01-02，
  
  网络出版日期：2009-10-30，
  
  纸质出版日期：2009-10-30
- 稿件说明：
移动端阅览
王娟娟;袁曦明;李予晋;尚淑娟;谢安;王永钱;. 共沉淀法制备PDP用红色荧光粉 (Y, Gd)BO3 : Eu3+的正交实验研究[J]. 液晶与显示, 2009,24(5): 645-649

WANG Juan-juan;YUAN Xi-ming;LI Yu-jin;SHANG Shu-juan;XIE An;WANG Yong-qian;. Preparation of Red Phosphor (Y, Gd)BO3 : Eu3+ by Coprecipitation Method with Orthogonal Test[J]. 液晶与显示, 2009,24(5): 645-649
王娟娟;袁曦明;李予晋;尚淑娟;谢安;王永钱;. 共沉淀法制备PDP用红色荧光粉 (Y, Gd)BO3 : Eu3+的正交实验研究[J]. 液晶与显示, 2009,24(5): 645-649 DOI：

WANG Juan-juan;YUAN Xi-ming;LI Yu-jin;SHANG Shu-juan;XIE An;WANG Yong-qian;. Preparation of Red Phosphor (Y, Gd)BO3 : Eu3+ by Coprecipitation Method with Orthogonal Test[J]. 液晶与显示, 2009,24(5): 645-649 DOI：

摘要

以Y

和硼酸为原料

草酸为沉淀剂

采用共沉淀法合成了PDP用红色荧光粉(Y

Gd)BO

: Eu

。同时

利用正交实验探讨了合成工艺条件对荧光粉相对发光强度的影响。实验确定了制备PDP用红色荧光粉(Y

Gd)BO

: Eu

的优化工艺条件:沉淀剂/金属离子总量为1.2 : 1;pH=8;离子混合超声20 min;沉淀超声1 h;650 ℃预烧1 h;950 ℃烧结2 h。采用PDP真空紫外测试系统、X射线衍射仪、环境扫描电镜对荧光粉进行了表征。结果表明:在优化工艺条件下所制备的荧光粉为六方晶系

空间群为P63/m

平均粒径约为300 nm。

Abstract

Red phosphor (Y

Gd)BO

: Eu

was prepared by coprecipitation method with Y

and H

as the starting material

oxalic acid as precipitant. The effect of the synthetic conditions on the relative luminescence intensity was discussed with orthogonal test. The optimal synthetic conditions were achieved as follows:

oxalic acid

cationic

＝1.2 : 1

pH=8

supersonic time of cation mixing was 20 min

super-sonic time of precipitation was 1 h

calcined temperature was 650 ℃ and the time was 1 h

sintering temperature was 950 ℃ and the time was 2 h. The phosphor was characterized by Vacuum Ultraviolet test system for PDP

XRD and ESEM

respectively. The results showed that the samples exhibited the same diffraction patterns as appeared in JCPDS card No.188-0356 corresponding to the intrinsic diffraction patterns of hexagonal structure of YBO

with the P63/m space group. The average particle size was about 300 nm.

关键词

Keywords

references

. 王林生, 文小强, 周健,等. 国内PDP用绿色荧光粉的研究进展 [J]. 江西有色金属, 2006, 20(4):17-20.

. 董岩, 蒋建清, 肖睿,等. (Y, Gd)BO3 : Eu3+荧光粉的合成及粒度控制 [J]. 中国稀土学报, 2004, 22(2):204-205.

. 邓新荣, 胡国荣, 彭忠东,等. PDP用红色荧光粉的研究进展 [J]. 材料导报 , 2006, 20 (2):40-43.

. 陶怡, 李岚, 王达健,等. PDP 荧光粉的优化研究 [J]. 天津理工大学学报, 2005, 21(4): 74-77.

. 韩芝隆. 概率论与数理统计 [M]. 北京: 化学工业出版社, 2000: 263-270.

. 宋宏伟.稀土掺杂氧化物纳米发光材料研究 [J]. 发光学报 ,2008, 29(6):921-936.

. 张睿, 顾牡, 刘小林, 等. 共掺杂效应对Y2O3 : Eu3+和Gd2O3: Eu3+发光影响的理论研究 [J]. 发光学报 , 2007, 28(3):383-389.

. 夏上达. 稀土发光和光谱理论的研究进展 [J]. 发光学报 ,2007, 28(4):465-479.

. 陈雪梅, 陈彩凤, 陈志刚. 超声沉淀法制备纳米Al2O3粉体 [J]. 中国有色金属学报 , 2003, 13(1):122-126.

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

氮(氧)化物荧光粉的合成与发光性能

LED用KZn₄（BO₃）₃：Eu³⁺荧光粉的合成与发光性能研究

新型Ba₂ZnS₃ : Cu荧光粉的合成及其发光性能