Research of Cu corrosion in 4-Mask process

Jin-chao BAI; Xiao-long LI; Hao HAN; Xiang-meng ZHANG; Tian-yu ZUO; Zu-mou WU; Xiang-qian DING; Yong-zhi SONG; Wei-tao CHEN

doi:10.3788/YJYXS20193402.0125

您当前的位置：

首页 >

文章列表页 >

Research of Cu corrosion in 4-Mask process

Materials and Device | 更新时间：2020-07-05

- Research of Cu corrosion in 4-Mask process
- Chinese Journal of Liquid Crystals and Displays Vol. 34, Issue 2, Pages: 125-129(2019)
- 作者机构：
  
  北京京东方显示技术有限公司, 北京 100176
- 作者简介：
- 基金信息：
- DOI：10.3788/YJYXS20193402.0125
  CLC： TN141.9
- Received：13 August 2018，
  
  Accepted：15 November 2018，
  
  Published：05 February 2019
- 稿件说明：
移动端阅览
Jin-chao BAI, Xiao-long LI, Hao HAN, et al. Research of Cu corrosion in 4-Mask process[J]. Chinese journal of liquid crystals and displays, 2019, 34(2): 125-129.
DOI：

Jin-chao BAI, Xiao-long LI, Hao HAN, et al. Research of Cu corrosion in 4-Mask process[J]. Chinese journal of liquid crystals and displays, 2019, 34(2): 125-129. DOI： 10.3788/YJYXS20193402.0125.

摘要

针对4-Mask工艺铜数据线腐蚀造成的锯齿状不良现象进行系统研究，发现铜腐蚀发生的工艺步骤和机理，并找到有效的措施。首先，通过显微镜对每道刻蚀工艺后铜数据线形貌进行观测，确定铜腐蚀发生的工艺步骤。接着，通过扫描电子显微镜和X射线电子能谱测量腐蚀生产物成分，对腐蚀机理提出合理解释。最后在铜腐蚀发生机理基础上，提出有效的改善措施。铜腐蚀是在有源半导体层干刻和光刻胶的灰化综合作用下发生，其主要产物为氧化铜、氯化铜。通过先进行灰化工艺然后进行有源半导体层干刻的工艺措施，在铜数据线两侧形成氧化铜保护膜，可以彻底改善铜腐蚀。改善措施可以解决铜腐蚀的问题，彻底消除铜数据线锯齿状不良。

Abstract

The jagged defect of copper data lines caused by corrosion of copper in 4-Mask process was investigated systematically

the steps and mechanism of copper corrosion were found

and the effective measures to improve copper corrosion were established. Firstly

the morphology of copper data lines after each etching process was observed by microscope to determine the process steps of copper corrosion. Then

the composition of corrosion products was confirmed by scanning electron microscopy (SEM) and X-ray electron spectroscopy (EDS)

and the corrosion mechanism was explained reasonably. Finally

based on the mechanism of copper corrosion

effective improvement measures were put forward. Copper corrosion occurs under the combined action of a-Si dry etching and photoresist ashing

and the main products of copper corrosion are CuO and CuCl

. CuO protective film is formed on both sides of copper data line by ashing process first and then a-Si dry etching

so copper corrosion can be completely improved. The improvement measures can solve the problem of copper corrosion and eliminate the jagged defect of copper data lines.

关键词

Keywords

references

谷至华.薄膜晶体管(TFT)阵列制造技术[M].上海:复旦大学出版社, 2007.

GU Z H. Thin Film Transistor ( TFT ) Array Manufacturing Technology [M]. Shanghai:Fudan University Press, 2007. (in Chinese)

刘翔, 陈旭, 谢振宇, 等.使用低电阻金属铝制造薄膜晶体管阵列信号电极[J].液晶与显示, 2009, 24(4):533-536.

LIU X, CHEN X, XIE Z Y, et al . Low resistant metal for thin film transistors[J]. Chinese Journal of Liquid Crystals and Displays , 2009, 24(4):533-536. (in Chinese)

TSAI W C, LAI J Y, TU K Y, et al . A novel barrierless Cu gate for TFT-LCD[J]. SID Symposium Digest of Technical Paper , 2006, 37(1):1181-1184.

SONG S X, LIU Y Z, MAO D L, et al . Diffusion barrier performances of thin Mo, Mo-N and Mo/Mo-N films between Cu and Si[J]. Thin Solid Films , 2005, 476(1):142-147.

SONG J H, KWON D J, KIM S G, et al . Advanced four-mask process architecture for the a-Si TFT array manufacturing method[J]. SID Symposium Digest of Technical Paper , 2002, 33(1):1038-1041.

白金超, 张光明, 郭总杰, 等.各膜层对光刻胶灰化的影响[J].液晶与显示, 2015, 30(4):616-620.

BAI J C, ZHANG G M, GUO Z J, et al . Effect of film layer on photoresist ashing[J]. Chinese Journal of Liquid Crystals and Displays , 2015, 30(4):616-620. (in Chinese)

刘翔, 王章涛, 崔祥彦, 等.液晶阵列四次光刻工艺中光刻胶灰化工艺的研究[J].真空科学与技术学报, 2008, 28(4):291-294.

LIU X, WANG Z T, CUI X Y, et al . Photoresist ashing in four-mask fabrication of thin film transistor liquid crystal display[J]. Chinese Journal of Vacuum Science and Technology , 2008, 28(4):291-294. (in Chinese)

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

No data

Related Author

No data

Related Institution

No data

AI问答

Address：No.3888 Dong Nanhu Road, Changchun, Jilin, China 130033 Postal code：130033
Tel：0431-86176059 Email：yjxs@ciomp.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 吉ICP备11002662号-17 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰