Guo-jing MA, Dan WANG, Shun-sha LU, et al. Application of optical alignment technology in TFT-LCD. [J]. Chinese Journal of Liquid Crystals and Displays 36(5):694-698(2021)
Guo-jing MA, Dan WANG, Shun-sha LU, et al. Application of optical alignment technology in TFT-LCD. [J]. Chinese Journal of Liquid Crystals and Displays 36(5):694-698(2021) DOI: 10.37188/CJLCD.2020-0324.
本文重点研究了降解型光控取向技术的制作工艺及其对产品性能的影响。通过分析不同光配向工艺参数下配向膜各向异性的数值可知,随着UV光光积量的增大和二次固化时间的延长,配向膜的各向异性值都有先升高后降低的趋势。测试材料在550 mJ/cm,2,和30 min的条件下,配向能力最优;配向膜材料二次固化温度在250 ℃以内时对配向性的影响是随温度升高,配向膜的各向异性值有直线上升趋势。通过改变光配向的工艺条件测试TFT特性的变化,发现完整的光配向工艺对TFT特性无明显影响。本文还分析了光配向形成的配向膜的低预倾角(约0.2°)对产品性能的影响,从结果可知,低预倾角下产品的对比度可达到1 500以上,与摩擦型产品对比提升了约50%。
The degradable optical alignment technology and its main effects on TFT-LCD are studied. The anisotropy of PI shows a trend from increasing to decreasing as the exposure dose increases and the main curing time extends. The anisotropy of PI, which is a common representation of the alignment ability of PI, performs best at 550 mJ/cm,2, ultraviolet treatment and 30 min curing time. In addition, the anisotropy of PI keeps increasing as the main curing temperature increases from 230 ℃ to 250 ℃. Results also demonstrate that the complete optical alignment has no obvious effect on the electrical properties of TFTs. Compared to rubbing process, optical alignment shows huge advantages of contract ratio. The contract ratio of optical alignment product is about 1 500, approximately 50% higher than that of rubbing product, due to the low pre-title angle (about 0.2°).
光配向紫外光配向膜各向异性TFT特性
optical alignmentultravioletpolyimideanisotropyTFT characteristics
马 群刚 . TFT-LCD原理与设计 , : 北京 电子工业出版社 , 2011 .
Q G MA . Principle and Design of TFT-LCD , : Beijing Publishing House of Electronics Industry , 2011 .
杨 宗顺 , 杨 夏梅 , 熊 奇 , 等 . 摩擦工艺不良的探究 . 液晶与显示 , 2019 . 34 ( 11 ): 1073 - 1078 . http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20193411.1073http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20193411.1073.
Z S YANG , X M YANG , Q XIONG , 等 . Research and solution of defects in rubbing process . Chinese Journal of Liquid Crystals and Displays , 2019 . 34 ( 11 ): 1073 - 1078 . http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20193411.1073http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20193411.1073.
周 波 , 王 祺 , 宋 勇志 , 等 . TFT-LCD中液晶取向异常亮点机理研究及改善 . 液晶与显示 , 2020 . 35 ( 2 ): 115 - 121 . http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20203502.0115http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20203502.0115.
B ZHOU , Q WANG , Y Z SONG , 等 . Research and improvement of bright dot caused by abnormal liquid crystal alignment on TFT-LCD . Chinese Journal of Liquid Crystals and Displays , 2020 . 35 ( 2 ): 115 - 121 . http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20203502.0115http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20203502.0115.
杨 德波 , 钟 野 , 毕 芳 , 等 . Mobile产品异物产生机理及改善研究 . 液晶与显示 , 2019 . 34 ( 8 ): 748 - 754 . http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20193408.0748http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20193408.0748.
D B YANG , Y ZHONG , F BI , 等 . Reduction and mechanism of particles on mobile products . Chinese Journal of Liquid Crystals and Displays , 2019 . 34 ( 8 ): 748 - 754 . http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20193408.0748http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20193408.0748.
栗 芳芳 , 汪 弋 , 陆 相晚 , 等 . 摩擦配向工艺对HADS产品像素漏光的影响分析 . 液晶与显示 , 2019 . 34 ( 3 ): 241 - 244 . http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20193403.0241http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20193403.0241.
F F LI , Y WANG , X W LU , 等 . Analysis of the effect of rubbing process on pixel leakage of HADS . Chinese Journal of Liquid Crystals and Displays , 2019 . 34 ( 3 ): 241 - 244 . http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20193403.0241http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20193403.0241.
李 继军 , 聂 晓梦 , 李 根生 , 等 . 平板显示技术比较及研究进展 . 中国光学 , 2018 . 11 ( 5 ): 695 - 710 . https://www.cnki.com.cn/Article/CJFDTOTAL-ZGGA201805001.htmhttps://www.cnki.com.cn/Article/CJFDTOTAL-ZGGA201805001.htm.
J J LI , X M NIE , G S LI , 等 . Comparison and research progress of flat panel display technology . Chinese Optics , 2018 . 11 ( 5 ): 695 - 710 . https://www.cnki.com.cn/Article/CJFDTOTAL-ZGGA201805001.htmhttps://www.cnki.com.cn/Article/CJFDTOTAL-ZGGA201805001.htm.
廖 燕平 , 宋 勇志 , 邵 喜斌 , 等 . 薄膜晶体管液晶显示器显示原理与设计 , : 北京 电子工业出版社 , 2016 .
Y P LIAO , Y Z SONG , X B SHAO , 等 . Thin Film Transistor Liquid Crystal Display , : Beijing Publishing House of Electronics Industry , 2016 .
张 春华 , 杨 正华 ,丁 孟贤 . 聚酰亚胺光控取向膜的研究现状 . 高分子通报 , 2002 . ( 6 ): 15 - 23 . https://www.cnki.com.cn/Article/CJFDTOTAL-GFZT200206002.htmhttps://www.cnki.com.cn/Article/CJFDTOTAL-GFZT200206002.htm.
C H ZHANG , Z H YANG , M X DING . Recent development in photoalignment polyimide films . Polymer Bulletin , 2002 . ( 6 ): 15 - 23 . https://www.cnki.com.cn/Article/CJFDTOTAL-GFZT200206002.htmhttps://www.cnki.com.cn/Article/CJFDTOTAL-GFZT200206002.htm.
张 万隆 , SRIVASTAVA A , ROGACH A , 等 . 半导体量子棒的光控取向技术进展 . 液晶与显示 , 2020 . 35 ( 5 ): 409 - 421 . http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20203505.0409http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20203505.0409.
W L ZHANG , A SRIVASTAVA , A ROGACH , 等 . Progress in photo-induced semiconductor quantum rods alignment . Chinese Journal of Liquid Crystals and Displays , 2020 . 35 ( 5 ): 409 - 421 . http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20203505.0409http://cjlcd.lightpublishing.cn/thesisDetails#10.3788/YJYXS20203505.0409.
J M GEARY , J W GOODBY , A R KMETZ , 等 . The mechanism of polymer alignment of liquid-crystal materials . Journal of Applied Physics , 1987 . 62 ( 10 ): 4100 - 4108 . DOI:10.1063/1.339124http://doi.org/10.1063/1.339124.
O YAROSHCHUK , Y REZNIKOV . Photoalignment of liquid crystals: basics and current trends . Journal of Materials Chemistry , 2012 . 22 ( 2 ): 286 - 300 . http://www.tandfonline.com/servlet/linkout?suffix=CIT0004&dbid=16&doi=10.1080%2F02678292.2018.1429027&key=10.1039%2FC1JM13485Jhttp://www.tandfonline.com/servlet/linkout?suffix=CIT0004&dbid=16&doi=10.1080%2F02678292.2018.1429027&key=10.1039%2FC1JM13485J.
洪 一凡 , 臧 金亮 , 刘 颖 , 等 . 偏光全息研究历程与展望 . 中国光学 , 2017 . 10 ( 5 ): 588 - 602 . https://www.cnki.com.cn/Article/CJFDTOTAL-ZGGA201705006.htmhttps://www.cnki.com.cn/Article/CJFDTOTAL-ZGGA201705006.htm.
Y F HONG , J L ZANG , Y LIU , 等 . Review and prospect of polarization holography . Chinese Optics , 2017 . 10 ( 5 ): 588 - 602 . https://www.cnki.com.cn/Article/CJFDTOTAL-ZGGA201705006.htmhttps://www.cnki.com.cn/Article/CJFDTOTAL-ZGGA201705006.htm.
梁 兆颜 , 闫 石 , 马 凯 , 等 . 液晶显示用取向材料聚甲基丙烯酸肉桂酰氧基乙酯的光控取向研究 . 发光学报 , 1999 . 20 ( 3 ): 217 - 223 . https://www.cnki.com.cn/Article/CJFDTOTAL-FGXB199903005.htmhttps://www.cnki.com.cn/Article/CJFDTOTAL-FGXB199903005.htm.
Z Y LIANG , S YAN , K MA , 等 . Study on photo alignment of cinnamate material 2(cinnamoyloxy)ethyl methacrylate for LCD using LPP method by UV light . Chinese Journal of Luminescence , 1999 . 20 ( 3 ): 217 - 223 . https://www.cnki.com.cn/Article/CJFDTOTAL-FGXB199903005.htmhttps://www.cnki.com.cn/Article/CJFDTOTAL-FGXB199903005.htm.
0
Views
173
下载量
0
CSCD
Publicity Resources
Related Articles
Related Author
Related Institution