Controlled Synthesis and Doping of Single-Crystalline 6H-SiC Nanowire and Its Optic Properties

FAN Yi; GAO Feng-mei; YANG Wei-you; JIANG Da-peng; ZHANG Li-gong

doi:null

您当前的位置：

首页 >

文章列表页 >

Controlled Synthesis and Doping of Single-Crystalline 6H-SiC Nanowire and Its Optic Properties

Material Physics & Chemistry | 更新时间：2020-08-12

- Controlled Synthesis and Doping of Single-Crystalline 6H-SiC Nanowire and Its Optic Properties
- Chinese Journal of Liquid Crystals and Displays Vol. 24, Issue 6, Pages: 804-808(2009)
- 作者机构：
  
  1. 中国科学院长春光学精密机械与物理研究所激发态物理重点实验室, 吉林长春 130033,E-mail:fany@ciomp.ac.cn
  2. 宁波工程学院材料工程研究所,浙江宁波,315016
- 作者简介：
- 基金信息：
- DOI：
  CLC： TB383.1
- Received：12 August 2009，
  
  Revised：02 January 1900，
  
  Published Online：30 December 2009，
  
  Published：30 December 2009
- 稿件说明：
移动端阅览
范翊;高凤梅;杨为佑;蒋大鹏;张立功. 单晶6H-SiC纳米线的可控掺杂及光学特性[J]. 液晶与显示, 2009,24(6): 804-808

FAN Yi;GAO Feng-mei;YANG Wei-you;JIANG Da-peng;ZHANG Li-gong. Controlled Synthesis and Doping of Single-Crystalline 6H-SiC Nanowire and Its Optic Properties[J]. 液晶与显示, 2009,24(6): 804-808
范翊;高凤梅;杨为佑;蒋大鹏;张立功. 单晶6H-SiC纳米线的可控掺杂及光学特性[J]. 液晶与显示, 2009,24(6): 804-808 DOI：

FAN Yi;GAO Feng-mei;YANG Wei-you;JIANG Da-peng;ZHANG Li-gong. Controlled Synthesis and Doping of Single-Crystalline 6H-SiC Nanowire and Its Optic Properties[J]. 液晶与显示, 2009,24(6): 804-808 DOI：

摘要

采用有机前驱体制备纳米材料工艺

制备出不同Al掺杂浓度的6H-SiC纳米线(Al/6H-SiC)。用HRTEM、EDX、XRD等对纳米线进行了表征

发现随着起始材料中异丙醇铝含量的增加

所制备的纳米线中的Al浓度也在增加

最高可达到1.25%

HRTEM显示晶格间距为0.26 nm和0.25 nm

对应为6H-SiC的(101)和(102)面间距

Si、C原子比为1 ∶ 1。拉曼光谱得到这种6H-SiC的声子能量为100 meV

由吸收光谱带边吸收外推计算得到Al/6H-SiC纳米线光学带隙

掺杂浓度越大

吸收边红移越大。

Abstract

Al-doped 6H-SiC nanowires (Al/6H-SiC) were successfully fabricated via catalyst-assisted pyro-lysis of polymeric precursor. The samples were characterized by HRTEM

EDS and XRD. The results showed that the doped concentrations were adjusted from 0.5% up to 1.25% with the Al concentrations in the precursors. The HRTEM pattern illustrated that the lattice fringe spacings are 0.26 nm and 0.25 nm. EDX shows the atom ratio of Si and C is 1 : 1. The XRD pattern demonstrated that Al-doping causes a decrease in the lattice parameters with Al concentration as compared with standard values. The optical properties of single-crystalline 6H-SiC nanowires with different Al doping levels were characterized by Raman and absorption spectra. The Raman spectra reveal that the phonon energy of the single-crystalline SiC nanowire is 100 meV. We estimated the optical absorption band-gap of nanowires from optical band-edge absorption. Al doping results in a red-shift on the optical absorption edge of SiC nanowire

thus it demonstrates a reduction of optical band gap.

关键词

Keywords

references

. Demir T, Renfro T E, Glosser R, et al. Optical characterization of n- and p-doped 4H-SiC by electroreflectance spectroscopy [J]. Appl. Phys. Lett., 2004, 84(18):3540-3542.

. Zhao Q Z, Ciobanu F, Malzer S, et al. Enhancement of optical absorption and photocurrent of 6H-SiC by laser surface nanostructuring [J]. Appl. Phys. Lett., 2007, 91(12):121107(1-3).

. Casady J B, Johnson R W. Status of silicon carbide (SiC) as a wide-bandgap semiconductor for high-temperature applications: A review [J]. Solid. State Electron., 1996, 39(10):1409-1422.

. Neudeck P G. Progress in silicon-carbide semiconductor electronics technology [J]. J. Electron. Mater., 1995, 24(4):283-8.

. Morkoc H, Strite S, Gao G B, et al. Large-band-gap SiC, Ⅲ-Ⅴ nitride, and Ⅱ-Ⅵ ZnSe-based semiconductor device technologies [J]. J. Appl. Phys., 1994, 76(3):1363-1398

. 陈德媛,钱波,徐骏,等.非晶碳化硅材料与光学微腔的制备与发光 [J]. 发光学报 ,2007,28(1):121-125.

. Chiu S C, Huang C W, Li Y Y. Synthesis of high-purity silicon carbide nanowires by a catalyst-free arc-discharge method [J]. J. Phys. Chem. C, 2007, 111(28):10294-10297.

. Niu J J, Wang J N. A simple route to synthesize scales of aligned single-crystalline SiC nanowires arrays with very small diameter and optical properties [J]. J. Phys. Chem. B, 2007, 111(17):4368-4373.

. Zhou W M, Liu X, Zhang Y F. Simple approach to beta-SiC nanowires: Synthesis, optical, and electrical properties [J]. Appl. Phys. Lett., 2006, 89(22):223124(1-3).

. Li Z J, Zhang J L, Meng A, et al. Large-area highly-oriented SiC nanowire arrays: Synthesis, raman, and photoluminescence properties [J]. J. Phys. Chem. B, 2006, 110(45):22382-22386.

. Ye H H, Titchenal N, Gogotsi Y, et al. SiC nanowires synthesized from electrospun nanofiber templates [J]. Adv. Mater., 2005, 17(12):1531-1535.

. Wu R B, Pan Y, Yang G Y, et al. Twinned SiC zigzag nanoneedles [J]. J. Phys. Chem. C, 2007, 111(17):6233-6237.

. Pol V G, Pol S V, Gedanken A, et al. Thermal decomposition of commercial silicone oil to produce high yield high surface area SiC nanorods [J]. J. Phys. Chem. B, 2006, 110(23):11237-11240.

. Xi G C, Liu Y K, Liu X Y, et al. Mg-catalyzed autoclave synthesis of aligned silicon carbide nanostructures [J]. J. Phys. Chem. B, 2006, 110(29):14172-14178.

. Yang W Y, Miao H Z, Xie Z P, et al. Synthesis of silicon carbide nanorods by catalyst-assisted pyrolysis of polymeric precursor [J]. Chem. Phys. Lett., 2004, 383(5-6):441-444.

. Lai H L, Wong N B, Zhou X T, et al. Straight beta-SiC nanorods synthesized by using C-Si-SiO2 [J]. Appl. Phys. Lett., 2000, 76(3):294-296.

. Xi G C, Peng Y Y, Wan S M, et al. Lithium-assisted synthesis and characterization of crystalline 3C-SiC nanobelts [J]. J. Phys. Chem. B, 2004, 108(52):20102-20104.

. Zou G F, Dong C, Xiong K, et al. Low-temperature solvothermal route to 2H-SiC nanoflakes [J]. Appl. Phys. Lett., 2006, 88(7):071913(1-3).

. Pei L Z, Tang Y H, Zhao H Z, et al. Formation mechanism of silicon carbide nanotubes with special morphology [J]. J. Appl. Phys., 2006, 100(4):046105(1-3).

. Pei L Z, Tang Y H, Chen Y W, et al. Preparation of silicon carbide nanotubes by hydrothermal method [J]. J. Appl. Phys., 2006, 99(11):114306(1-3).

. Mpourmpakis G, Froudakis G E, Lithoxoos G P, et al. SiC nanotubes: A novel material for hydrogen storage [J]. Nano Lett., 2006, 6(8):1581-1583.

. Zhang D Q, Alkhateeb A, Han H M, et al. Norton, silicon carbide nanosprings [J]. Nano Lett., 2003, 3(7):983-987.

. Liu Z Y, Ci L J, Jin-Phillipp N Y, et al. Vapor-solid reaction for silicon carbide hollow spherical nanocrystals [J]. J. Phys. Chem. C, 2007, 111(34):12517-12521.

. Gao F M, Yang W Y, Wang H T, et al. Controlled Al-doped single-crystalline 6H-SiC nanowires, crystal growth & design [J]. 2008, 8(5):1461-1464.

. Spanier Jonathan E. Optical and electrochemical properties of nanoscale materials . Columbia, USA:Graduate School of Science and Arts, Columbia University, 2001.

. Okumura H, Sakuma E, Lee J H, et al. Raman scattering of SiC: Application to the identification of heteroepitaxy of SiC polytypes [J]. J. Appl. Phys., 1987,61(3):1134-1136.

. Zhao Q Z, Ciobanu F, Malzer S, et al. Enhancement of optical absorption and photocurrent of 6H-SiC by laser surface nanostructruing [J]. Appl. Phys. Lett., 2007, 91(12):121107(1-3).

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research progress on performance regulation of lyotropic chromonic liquid crystals

PEDOT: PSS doped with cesium chloride for highly efficient and bright metal halide perovskite light-emitting diodes

Preparation of Highly Conductive Polymer PEDOT:PSS by Post-Treatment

Effect of Annealing Temperature on Structure and Optical Properties of Sheet-like ZnO Crystals

Electroluminescent Spectral Stability of Multilayer Doping White Organic Light-Emitting Diodes

Related Author

LU Yanqing

LI Bingxiang

LI Jungang

YANG Zhaoyan

OU Zijian

Ming-liang LI

Ke-bin LIN

Jian-xun LU

Related Institution

College of Electronic and Optical Engineering & College of Flexible Electronics（Future Technology）， Nanjing University of Posts and Telecommunications

National Laboratory of Solid State Microstructures， College of Engineering and Applied Sciences， Nanjing University

Sichuan Research Center of New Materials, Institute of Chemical Materials, China Academy of Engineering Physics

Institute of Luminescent Materials and Information Displays, College of Materials Science and Engineering, Huaqiao University

Department of Chemistry, School of Science, Beijing Jiaotong University

AI问答

Address：No.3888 Dong Nanhu Road, Changchun, Jilin, China 130033 Postal code：130033
Tel：0431-86176059 Email：yjxs@ciomp.ac.cn
Technical support is provided by Beijing Founder electronics co., LTD 吉ICP备11002662号-17 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰